print small

Participating Countries:

Australia

Austria

Belgium

Bulgaria

Canada

Cyprus

Czech Republic

Denmark

European Commission

France

Germany

Greece

Hungary

Ireland

Israel

Italy

Norway

Poland

Portugal

Romania

Russian Federation

Serbia

Slovakia

Slovenia

Spain

Sweden

Switzerland

Turkey

Ukraine

United Kingdom

United States of America

COST is supported by the EU Framework Programme Horizon 2020
This website is supported by COST

Orla Carron

Early stage researcher* (ESR)/ Early Career Investigator (ECI)
PhD student
Period of mission: 28-10-2016 to 02-12-2016
Host institution: Laboratoire de Chimie des Polymeres Organiques (LCPO) UMR5629 Université de Bordeaux

Home institution:

Towards the synthesis of magnetic-Large Hybrid Vesicles (m-LHVs)

 In this project we developed novel membrane stabilized nanocomposites, with magnetic nanoparticles (MNPs) bound directly into the membrane to maximize hyperthermic response. Induced heat should affect the vesicle permeability, allowing for specific, localized drug release in tumor tissue. The approaches below were developed to produce a library of m-LHVs. A signifiant positive is that these processes can be easily expanded to prepare hybrid vesicles, including lipids.

1. Synthesis of PB-PEO or PDMS-(PEO)2 based polymer vesicles

a. Rehydration method for the formation of Large Unilameller Vesicles (LUVs); as multilamellar vesicles were formed these were extruded. The method developed can be used for a range of materials; including m-LUVs (magnetic LUCs), LHVs (hybrids) and m-LHVs.

b. Emulsion-Evaporation Method for LUVs; the vesicles formed were typically less monodisperse than from rehydration, however as no multilameller vesicles are formed, extrusion was not needed. Again a range of sizes were formed.

c. Electroformation of Giant Unilameller Vesicles (GUVs); importantly this procedure can be easily applied to obtain GHVs.

2. Synthesis of PDMS-PEO2 based polymer vesicles

d. Emulsion-evaporation was successfully applied, however the vesicles were less monodisperse.

In summary vesicles of three different compositions were successfully prepared; (i) PDMS-g-(PEO)2 (3KDa) (ii) PDMS(5kDa)-b-(PEO)2 vesicles; (iii) OA-coated MNPs in PBut-b-PEO vesicles, with typical MNP feed weight ratio of 10, but up to 3wt% (iii). Primary characterisation of the suspensions was completed at LCPO, see Figure. Over the coming months the use of smaller MNPs and improved coating will be evaluated. AC-field hyperthermia and NMR measurements will be undertaken to confirm the particles are localised in the membrane and to evaluate the effect of composition/structure on heating efficiency and MRI contrast potential. We will also assess domain formation at nanoscale by FRET and SANS.